Abstract

This guide covers standard specification for a number of grades of nominal-wall-thickness, welded ferritic and martensitic stainless steel tubing for general corrosion-resisting and high-temperature service. The steel shall conform to the required chemical composition for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, molybdenum, aluminum, copper, nitrogen, titanium, and columbium. The number of tubes in a lot heat treated by the continuous process shall be determined from the size of the tubes. The steel shall conform to the following tensile properties: tensile strength, yield strength, and elongation. The tubes shall have a hardness number that will not exceed the prescribed Brinell and Rockwell hardness values. Several mechanical tests shall be conducted, namely: tension test; flaring test (for seamless tubes); flange test (for welded tubes); hardness test; reverse flattening test; intergranular corrosion test; and hydrostatic or nondestructive electric test.

This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASTM does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.

1. Scope

1.1 This specification covers a number of grades of nominal-wall-thickness, stainless steel tubing for general corrosion-resisting and high-temperature service. Most of these grades are commonly known as the straight-chromium types and are characterized by being ferromagnetic. Two of these grades, TP410 and UNS S 41500 (Table 1), are amenable to hardening by heat treatment, and the high-chromium, ferritic alloys are sensitive to notch-brittleness on slow cooling to ordinary temperatures. These features should be recognized in the use of these materials. Grade TP439 is used primarily for hot-water tank service and does not require post-weld heat treatment to prevent attack of the heat affected zone.

1.2 An optional supplementary requirement is provided, and when desired, shall be so stated in the order.

1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the M designation of this specification is specified in the order.

2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.

ASTM Standards

A480/A480M Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip

A763 Practices for Detecting Susceptibility to Intergranular Attack in Ferritic Stainless Steels

A1016/A1016M Specification for General Requirements for Ferritic Alloy Steel, Austenitic Alloy Steel, and Stainless Steel Tubes

E213 Practice for Ultrasonic Testing of Metal Pipe and Tubing

E273 Practice for Ultrasonic Testing of the Weld Zone of Welded Pipe and Tubing

Keywords

ferritic stainless steel; seamless steel tube; stainless steel tube; steel tube; welded steel tube
; Ferritic steel tube--specifications; Martensitic stainless steel tube--specifications; Seamless steel tube--specifications; Stainless steel tube--specifications; Welded steel tube--specifications;

ICS Code

ICS Number Code 23.040.10 (Iron and steel pipes)

DOI: 10.1520/A0268_A0268M-10

ASTM International is a member of CrossRef.

ASTM A268 / A268M